PC、243R聚碳酸酯

詳細(xì)內(nèi)容：PC、243R聚碳酸酯建筑上用作中空筋雙壁板、暖房玻璃等；在紡織行業(yè)用作紡織紗管、紡織機軸瓦等；日用方面作奶瓶、餐具、玩具、模型、LED燈外殼和手機外殼等。密度 --- ASTM D-792 0.043 lb/in3 吸水率 --- ASTM D-570 0.15-0.58 % 熔體流動速率 --- ASTM D-1238 10.5 g/10min 物理性能 模具收縮率 --- ASTM D-955 5-7 in/inE-3 比重 --- ASTM D-792 1.20 --- 阻燃性 V-2 UL 94 0.058 inch 阻燃性 V-0 UL 94 0.240 inch 機械性能 拉伸屈服強度 --- ASTM D-638 9000 Psi 拉伸斷裂強度 --- ASTM D-638 9500 Psi 拉伸屈服伸長率 --- ASTM D-638 7 % 拉伸斷裂伸長率 --- ASTM D-638 110 % 屈服彎曲強度 --- ASTM D-790 13500 Psi 屈服彎曲模量 --- ASTM D-790 340000 Psi 壓縮強度 --- ASTM D-695 12500 Psi 壓縮模量 --- ASTM D-695 345000 Psi 剪切強度 --- ASTM D-732 6000 Psi 剪切模量 --- ASTM D-4065 114000 Psi 洛氏硬度 --- ASTM D-785 70 M scale 洛氏硬度 --- ASTM D-785 118 R scale IZOD無缺口沖擊強度 73�H ASTM D-4812 60 ft-lb/in IZOD缺口沖擊強度 73�H ASTM D-256 15 ft-lb/in 拉伸強度 --- ASTM D-1822 260 ft-lb/in2 電氣性能 體積電阻率 --- ASTM D-527 >1017 Ω.cm 介電強度 --- ASTM D-149 380 V/mil 介電常數(shù) 60Hz ASTM D-150 3.17 --- 損耗因數(shù) 1MHz ASTM D-150 0.0100 --- 介電常數(shù) 1MHz ASTM D-150 2.96 --- 損耗因數(shù) 60Hz ASTM D-150 0.0009 --- 熱 性 能 脆化溫度 --- ASTM D-746 200 --- 維卡軟化點 --- ASTM D-1525 310 --- 熱變形溫度 66Psi ASTM D-648 280 --- 熱變形溫度 264Psi ASTM D-648 270 --- 熱傳導(dǎo)率 --- ASTM C-177 0.19 W/m.c 其它性能 折射指數(shù) --- ASTM D-542 1.586 --- 光傳送 --- ASTM D-1003 88 % 混濁 --- ASTM D-1003 1.0 % 磨損 --- ASTM D-1044 10 mg/1000cy 氧指數(shù) --- ASTM D-2863 25 % 制備編輯 聚碳酸酯紡織紗管的生產(chǎn)，選用光氣法生產(chǎn)的PC為原料，其中新料為80%，再生料為20%。其生產(chǎn)工藝流程如下： 配料→干燥→注射→修整→拋光→熱處理→制品。 烘箱干燥溫度115-120℃， 16-20小時，物料在料盤上厚度為30毫米以下，使樹脂含水量在0.03%以下。